Material Technology:
FDM Premium
Material Group
Technopolymers
All uploads are secure and confidential
PA6 CF is a composite material based on Polyamide 6 reinforced with short carbon fibers, designed to offer high performance in applications with high mechanical stress. The carbon fibers provide the material with superior mechanical strength, stiffness, and thermal stability compared to virgin polyamide. Characterized by low deformation and high dimensional stability, and resistant to a wide range of hydrocarbons, it is ideal for applications in sectors such as aviation, motorsports, and manufacturing for the production of high-performance structural components and tooling.
Alternative namings
-
Material Technology
FDM Premium
-
Material Group
Technopolymers
-
Native color
black
-
Elastic modulus
2.6-13 GPa
-
Yield stress
-
Tensile strength
34-171 MPa
-
Elongation at break
1.58-1.6 %
-
Hardness
-
Density
1.232 g/cm³
-
Melting temperature
-
Maximum service temperature
-
Thermal conductivity
-
Porosity
-
Minimum roughness Ra
18 µm
-
Tolerance
±0.5% (±0.5 mm) mm
-
Layer height
-
Minimum detail achievable
1.2-1.5 mm
-
Min Dimension [X]
-
Max Dimension [X]
500 mm
-
Min Dimension [Y]
-
Max Dimension [Y]
500 mm
-
Min Dimension [Z]
-
Max Dimension [Z]
500 mm
-
Flexural strength
-
Degradation temperature
-
Flexural modulus
-
Flamability
-
Impact strength
-
Water absorption
-
Izod impact notched
-
Purity
-
Charpy impact
-
Electrical conductivity
-
Glass transition temperature
-
Surface resistance
-
Heat deflection temperature 045 mpa
-
Volume resistivity
-
Heat deflection temperature 182 mpa
110 °C
-
Name
Material Technology
Material Group
All uploads are secure and confidential