PA12 GF
PA12 GF is a polyamide 12-based technopolymer reinforced with glass fibers. This formulation offers higher rigidity, mechanical resistance, and dimensional stability compared to standard PA12, making it suitable for applications requiring higher strength and rigidity. Thanks to SLS technology, PA12 GF can be used to produce complex components with precise details and uniform surfaces, ideal for industrial applications that require high performance and wear resistance.
Alternative namings
-
Material Technology
SLS
-
Material Group
Technopolymers
-
Native color
White/Off-white
-
Mechanical Properties
Elastic modulus
2.5-4.068 GPa
-
Yield stress
27 MPa
-
Tensile strength
26-57 MPa
-
Elongation at break
1.4-9 %
-
Hardness
77-80 Shore D
-
Physical Properties
Density
1.22-1.49 g/cm³
-
Melting temperature
-
Maximum service temperature
-
Thermal conductivity
0.47 W/m·K
-
Porosity
-
Geometric Properties
Minimum roughness Ra
8-10 µm
-
Tolerance
±0.3% (±0.3mm) mm
-
Layer height
-
Minimum detail achievable
1 mm
-
Dimensions
Min Dimension [X]
-
Max Dimension [X]
550 mm
-
Min Dimension [Y]
-
Max Dimension [Y]
550 mm
-
Min Dimension [Z]
-
Max Dimension [Z]
750 mm
-
Other
Flexural strength
37-73 MPa
-
Degradation temperature
-
Flexural modulus
2.9-3.106 GPa
-
Flamability
-
Impact strength
-
Water absorption
0.22 %
-
Izod impact notched
-
Purity
-
Charpy impact
-
Electrical conductivity
-
Glass transition temperature
-
Surface resistance
3.2x1011 Ω
-
Heat deflection temperature 045 mpa
157-179 °C
-
Volume resistivity
-
Heat deflection temperature 182 mpa
96-134 °C
-
Check out other materials
Name
Material Technology
Material Group
PA12 FR
SLS
-
Polymers
-
PA12 ALU
SLS
-
Technopolymers
-
PA12
SLS
-
Polymers
-
TPU
SLS
-
Elastomers
-
Get started and turn your parts into reality
All uploads are secure and confidential