PA12 GB
Material Technology:
MJF
Material Group
Technopolymers
All uploads are secure and confidential
PA12 GB
PA12 GB (Glass Beads) is a nylon material for Multi Jet Fusion, enriched with glass beads that improve rigidity and structural integrity. This material is loaded with 40% glass beads, which reduces warping during the printing process and over the product's lifetime. PA12 GB is ideal for flat and large parts prone to warping during MJF production, and for functional parts requiring high resistance and dimensional accuracy.
Alternative namings
-
Material Technology
MJF
-
Material Group
Technopolymers
-
Native color
gray
-
Mechanical Properties
Elastic modulus
2.5 GPa
-
Yield stress
47.5 MPa
-
Tensile strength
30 MPa
-
Elongation at break
10 %
-
Hardness
82 Shore D
-
Physical Properties
Density
1.3 g/cm³
-
Melting temperature
186 °C
-
Maximum service temperature
-
Thermal conductivity
-
Porosity
-
Geometric Properties
Minimum roughness Ra
8 µm µm
-
Tolerance
±0.3% (±0.2 mm) mm
-
Layer height
-
Minimum detail achievable
0.5 mm
-
Dimensions
Min Dimension [X]
-
Max Dimension [X]
380 mm
-
Min Dimension [Y]
-
Max Dimension [Y]
284 mm
-
Min Dimension [Z]
-
Max Dimension [Z]
380 mm
-
Other
Flexural strength
57.5 MPa
-
Degradation temperature
-
Flexural modulus
2.4 GPa
-
Flamability
UL94 HB
-
Impact strength
-
Water absorption
1.7 %
-
Izod impact notched
3 kJ/m2
-
Purity
-
Charpy impact
-
Electrical conductivity
-
Glass transition temperature
-
Surface resistance
-
Heat deflection temperature 045 mpa
174 °C
-
Volume resistivity
1013 Ω·m
-
Heat deflection temperature 182 mpa
114 °C
-
Check out other materials
Name
Material Technology
Material Group
PA12 White
MJF
-
Polymers
-
PA12
MJF
-
Polymers
-
PA12 GB
MJF
-
Technopolymers
-
TPU
MJF
-
Elastomers
-