Material Technology:
SLA
Material Group
Resin
All uploads are secure and confidential
PP Like is an ultra-resistant plastic material with exceptional durability, precision, and aesthetics, ideal for replacing CNC-machined polypropylene and ABS items. Easy and fast to work with, it offers physical properties similar to plastics like ABS and PP, making it perfect for functional prototypes in demanding applications and short-term production projects. This material has an aesthetic finish very similar to a final production part with extraordinary impact resistance, precision, and thermal resistance above 60°C, ideal for functional prototypes, short-term production projects, and CNC-machined item replacements.
Alternative namings
-
Material Technology
SLA
-
Material Group
Resin
-
Native color
grey
-
Elastic modulus
1.79-1.98 GPa
-
Yield stress
-
Tensile strength
38-44 MPa
-
Elongation at break
14-22 %
-
Hardness
86 Shore D
-
Density
1.19 g/cm³
-
Melting temperature
-
Maximum service temperature
-
Thermal conductivity
-
Porosity
-
Minimum roughness Ra
1.6 µm
-
Tolerance
±0.2 mm<100 mm; ±0.2 % >100 mm mm
-
Layer height
0.1 mm
-
Minimum detail achievable
0.5-0.7 mm
-
Min Dimension [X]
-
Max Dimension [X]
1350 mm
-
Min Dimension [Y]
-
Max Dimension [Y]
745 mm
-
Min Dimension [Z]
-
Max Dimension [Z]
500 mm
-
Flexural strength
52-71 MPa
-
Degradation temperature
-
Flexural modulus
1.52-2.07 GPa
-
Flamability
-
Impact strength
35-52 J/m
-
Water absorption
-
Izod impact notched
-
Purity
-
Charpy impact
-
Electrical conductivity
-
Glass transition temperature
70-74 °C
-
Surface resistance
-
Heat deflection temperature 045 mpa
62 °C
-
Volume resistivity
-
Heat deflection temperature 182 mpa
54 °C
-