Al 5083
Material Technology:
CNC
Material Group
Aluminum Alloys
All uploads are secure and confidential
Al 5083
Aluminum 5083 is an aluminum-magnesium alloy characterized by excellent corrosion resistance, especially in marine environments, and high mechanical strength. Due to its good machinability and weldability, it is used in applications such as ship hulls, cryogenic tanks, and transportation structures. CNC technology enables the production of high-precision components with a superior surface finish while maintaining the mechanical properties and lightweight nature of the material.
Alternative namings
Peraluman / 9005/5 / AlMg4.5Mn / 3.3547 / A-G4.5MC / P-AlMg4.5
-
Material Technology
CNC
-
Material Group
Aluminum Alloys
-
Native color
natural
-
Mechanical Properties
Elastic modulus
71 GPa
-
Yield stress
110 MPa
-
Tensile strength
275 MPa
-
Elongation at break
16 %
-
Hardness
75 HB
-
Physical Properties
Density
2.66 g/cm³
-
Melting temperature
570 °C
-
Maximum service temperature
80-100 °C
-
Thermal conductivity
170 W/m·K
-
Porosity
-
Geometric Properties
Minimum roughness Ra
1.6 - 3.2 µm
-
Tolerance
2768 classe fine (f) e media (m) mm
-
Layer height
-
Minimum detail achievable
1 mm
-
Dimensions
Min Dimension [X]
6 mm
-
Max Dimension [X]
500 mm
-
Min Dimension [Y]
6 mm
-
Max Dimension [Y]
500 mm
-
Min Dimension [Z]
6 mm
-
Max Dimension [Z]
400 mm
-
Other
Flexural strength
-
Degradation temperature
-
Flexural modulus
-
Flamability
-
Impact strength
-
Water absorption
-
Izod impact notched
-
Purity
-
Charpy impact
-
Electrical conductivity
105-120 %IACS
-
Glass transition temperature
-
Surface resistance
-
Heat deflection temperature 045 mpa
-
Volume resistivity
-
Heat deflection temperature 182 mpa
-